We keep on with our business spirit of "Quality, Performance, Innovation and Integrity". We goal to create much more worth for our customers with our rich resources, state-of-the-art machinery, experienced workers and exceptional providers for Toe-Puff, Adhesive Series, Pu Grouting Material, Items won certifications with the regional and international primary authorities. For far more detailed information, please contact us!

China wholesale Molded Foam - Pu Safety Shoe Sole System – INOV Detail:

Pu Safety Shoe Sole System

INTRODUCTION

PU Safety shoe-sole system is used to make safety shoe outsoles and inner soles. It is polyester-based PU system material, consist of four components, polyol, ISO, hardner and catalyst. The processing of the system is two components. The catalyst, harder, blowing agent and pigment should be mixed thoroughly with the polyol component EXD-3270A, then mix with ISO component EXD-3119B for making final wares.

PHYSICAL PROPERTIES

A, Inner soles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	85~88
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.35~0.4
Mould temperature（℃）	45~55
Product density（g/cm³）	0.5~0.55
Hardness（Shore A）	55~65
Demould time（min）	3
Elongation at break （%）	≥550
Tear strength（KN/m）	≥22
Tensile strength （MPa）	≥6.0
Ross flexing room temperature	50,000 times no crack

B, Outsoles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	82~85
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.55~0.6
Mould temperature（℃）	45~55
Product density（g/cm³）	0.6~0.8
Hardness（Shore A）	65~75
Demould time（min）	3
Elongation at break （%）	≥600
Tear strength（KN/m）	≥28
Tensile strength （MPa）	≥7.3
Ross flexing room temperature	50,000 times no crack
Demould time(min)	3
Product density(g/cm³)	0.2~0.3
Hardness(Shore C)	30~40
Tensile strength(MPa)	0.45-0.50
Tear strength(KN/m)	2.50-2.60
Elongation(%)	280-300

Product detail pictures:

Related Product Guide:

Our team through qualified training. Skilled professional knowledge, powerful sense of support, to satisfy the support desires of consumers for China wholesale Molded Foam - Pu Safety Shoe Sole System – INOV , The product will supply to all over the world, such as: Borussia Dortmund, Albania, Hungary, Satisfaction and good credit to every customer is our priority. We focus on every detail of order processing for customers till they have received safe and sound solutions with good logistics service and economical cost. Depending on this, our solutions are sold very well in the countries in Africa, the Mid-East and Southeast Asia.

Eda Base Eda

Memory Foam

Molded Foam

Polyurethane

This is the first business after our company establish, products and services are very satisfying, we have a good start, we hope to cooperate continuous in the future!