With advanced technologies and facilities, strict good quality manage, reasonable rate, superior assistance and close co-operation with shoppers, we have been devoted to supplying the very best price for our consumers for Mdi Elastomer Mdi, Mdi Prepolymer Mdi, Anti Uv, We guaranteed high quality, if clients were not satisfied with the products' quality, you can return inside 7days with their original states.

Chinese wholesale Pu Adhesives - Pu Safety Shoe Sole System – INOV Detail:

Pu Safety Shoe Sole System

INTRODUCTION

PU Safety shoe-sole system is used to make safety shoe outsoles and inner soles. It is polyester-based PU system material, consist of four components, polyol, ISO, hardner and catalyst. The processing of the system is two components. The catalyst, harder, blowing agent and pigment should be mixed thoroughly with the polyol component EXD-3270A, then mix with ISO component EXD-3119B for making final wares.

PHYSICAL PROPERTIES

A, Inner soles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	85~88
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.35~0.4
Mould temperature（℃）	45~55
Product density（g/cm³）	0.5~0.55
Hardness（Shore A）	55~65
Demould time（min）	3
Elongation at break （%）	≥550
Tear strength（KN/m）	≥22
Tensile strength （MPa）	≥6.0
Ross flexing room temperature	50,000 times no crack

B, Outsoles of safety shoe-sole preparing method:

Items	EXD-3270A	EXD-3119B
Ratio（weight ratio）	100	82~85
Material temperature（℃）	45~50	45~50
Rise time（s）	5~7
Tack free time（s）	30~50
Free foam density （g/cm³）	0.55~0.6
Mould temperature（℃）	45~55
Product density（g/cm³）	0.6~0.8
Hardness（Shore A）	65~75
Demould time（min）	3
Elongation at break （%）	≥600
Tear strength（KN/m）	≥28
Tensile strength （MPa）	≥7.3
Ross flexing room temperature	50,000 times no crack
Demould time(min)	3
Product density(g/cm³)	0.2~0.3
Hardness(Shore C)	30~40
Tensile strength(MPa)	0.45-0.50
Tear strength(KN/m)	2.50-2.60
Elongation(%)	280-300

Product detail pictures:

Related Product Guide:

The key to our success is "Good Product or service High quality, Reasonable Rate and Efficient Service" for Chinese wholesale Pu Adhesives - Pu Safety Shoe Sole System – INOV , The product will supply to all over the world, such as: Burundi, Jakarta, Chile, Our company is working by the operation principle of "integrity-based, cooperation created, people oriented, win-win cooperation". We hope we can have a friendly relationship with businessman from all over the world.