Donfoam 603 ECOMATE isiseko kuxubana polyols
Donfoam 603 ECOMATE isiseko kuxubana polyols
ISINGENISO
"Wood mbumbulu" isakhiwo amagwebu, uhlobo olutsha nangokukrola zokwenziwa, Donfoam 603 ukusetyenziswa ECOMATE njengoko bevuthela arhente. It has amandla aphezulu ngoomatshini kunye lukhuni, inkqubo udini elula, kahle eliphezulu imveliso kunye nenkangeleko entle.
Iimpawu zezi zilandelayo,
1. impahla uphindaphindo yokubumba kakhulu. Ku nga kuphela kunokutshintsha ubungakanani ethile imilo, kodwa usibumba nempilo iinkuni ukuguda noburhabaxa kwakunye nezinye iziyilo, ngezivakalisi ezipheleleyo
2. imbonakalo kwaye uzive kufutshane iinkuni, nenokuthi uncwelwe, zibethelelwe, seligrunjiwe, yaye zaba nemikrolo iipateni okanye zokwakha.
3. zomngundo ingaba i-alumuniyam okanye intsimbi, kunye lesilicon irabha, epoxy intlaka okanye ezinye nentlaka, ezo iindleko ephantsi machining lula.
4. Inkqubo olulula, fast, ukusebenza eliphezulu abafanelekayo.
5. iimpawu zomzimba ngomatshini yenye zomthi amagama kangangoko eziveliswa Polymer ezahlukeneyo. impahla Physical ungalawuleka ngokulungisa ifomula.
EKA ZOMZIMBA
imbonakalo Ixabiso Hydroxyl mgKOH / g Viscosity 25 ℃ mPa.s Density 20 ℃ g / ml lobushushu yokugcina Inyanga ukuzinza Ukugcinwa |
mthubi Ukukhanya ulwelo brown tyheli viscous 250-400 800-1500 1.10 ± 0,02 10-25 6 |
UMLINGANISELO OLUCETYISWAYO
|
pbw |
DFM-103 polyols Isocyanate |
100 100-105 |
Reactivity Iimpawu (ixabiso Eyona kuyahlukahlukana njengoko nganye iimeko yokwenza)
Rise ixesha s Gel ixesha s Oku- free time s Ukuxinana Free kg / m3 |
50-70 140-160 200-220 60-300 |
ngomdlalo amagwebu
mninzi udini amandla enomva amandla Compressive Tensile Strength umphezulu amandla ratio siyehla |
Kg / m3 MPA MPA MPA Shore D % |
100-400 7-10 5-7 5 35-70 ≤0.3 |