Shoe pu Upper cusbi
Shoe pu Upper cusbi
TIRADA
nidaamka Tani waa ka kooban yahay afar qaybood, polyol, ISO, Asagoo arigtadaa ka wakiilka iyo Hannaan.
Sifooyinka
Dhexgalo Heerkulka 30 ~ 40 ℃, Daaweynta Heerkulka 80 ~ 90 ℃, waqti Demould 8 ~ 10 min (hagaajin), ka darantahay ingeega, ee alaabta la dhammeeyayna laga beddeli karin beddelo ratio qalabka of qayb A + C / B.
Bakhaarka
Ku kaydi in qabow iyo meel qalalan. Haddii aadan isticmaali karin hal durbaan ilaa hal mar, fadlan buuxi gaaska Nitrogendoksid iyo sidoo xir durbaan. Nolosha shelf ee xirxirida asalka ah waa 6 bilood.
JIRKA guryaha
beegyada uu cadaanyo |
|||||
Dhammeeyayna Product engegnaantiinna / Shore A |
70 |
74 |
79 |
82 |
|
mass ratio |
DX3520-B |
62 |
68 |
75 |
80 |
DX3580-A |
97 |
96 |
95 |
94 |
|
DX3580-C |
3 |
4 |
5 |
6 |
|
Hannaan / DX3580-A (%) |
0,29 |
0,27 |
0,25 |
0,25 |
|
Wakiilka Defoaming / DX3580-A (%) |
0.45 |
0.47 |
0.49 |
0,53 |
|
waqti gel / min |
3 |
3 |
3 |
3 |
Farsamo Guryaha ee alaabta la dhammeeyayna |
||||
Engegnaantiinna / Shore A |
70 |
74 |
79 |
82 |
xoog siligga / MPA |
35 |
44 |
47 |
49 |
100% Modulus / MPA |
2.2 |
2.8 |
3.9 |
5.4 |
300% Modulus / MPA |
4.6 |
6.5 |
8.5 |
9.8 |
Ultimate muruqa /% |
540 |
520 |
500 |
490 |
Xoog Tear (Iyada oo aan Nick) / (Kn / m) |
56 |
66 |
76 |
89 |
Xoog Tear (La Nick) / (Kn / m) |
12 |
17 |
22 |
35 |