Donpanel tse 413 CP / IP botlaaseng motsoako polyols bakeng Pure
Donpanel tse 413 CP / IP botlaaseng motsoako polyols bakeng Pure
ke NTRODUCTION
DonPanel tse 413 ke mofuta oa motsoako polyether polyols le cyclopentane ka a ntsha lehulo moemeli, ho nka polyol e le lintho tse bonahalang ka sehloohong e tala 'me e kopane le e khethehileng moemeli ea thusang. Ho loketse kwahelang mogote ea ho haha mapolanka, mapolanka batang poloko le tse ling tse products.The kettle sehlahisoa lokisitsoeng ke itšoara ka isocyanate o na le le menyetla e latelang:
- Ha ho la sethopo e le hantle le ha e senya lera la ozone
- Good fluidity le junifomo bubble segokanyipalo
- Excellent kwahelang, tlhakore botsitso le mamarello
thepa ea moaho
DonPanel tse 413 |
|
Ponahalo e Hydroxyl boleng mgKOH / g,
Matla e tiileng e qamathelang (25 ℃) mPa.S Segokanyipalo (20 ℃) g, / ml tse Storage mocheso ℃ Storage likhoeli botsitso |
Khanya bosehla bonaletsang viscous mokelikeli 300-400 300-400 1.04-1.12 10-25 6 |
Recommended karo-karolelano
|
PBW |
DonPanel tse 413 |
100 |
Isocyanate |
110-130 |
THEKNOLOJI AND REACTIVITY (boleng hantle fapana ho itšetlehile ka maemo a lokisa)
Manual Remix |
phahameng khatello ea |
|
Raw tse bonahalang mocheso ℃
CT S gt solo ya no S TFT S Free segokanyipalo Kg / limithara 3 |
20-25 10-50 80-200 120-280 23-28 |
20-25 10-40 60-160 100-240 23-28 |
bubble liketso
hlobo segokanyipalo
sekhahla haufi-seleng ea Thermal conductivity (10 ℃) Compression matla) Tlhakore botsitso 24h -20 ℃ 24h 100 ℃ Flammability |
GB / T 6343 GB / T 10799 GB / T 3399 GB / T 8813 GB / T 8811
GB / T 8624 |
≥42 Kg / m3 ≥90% ≤22mW / mk la ≥150 KPa ≤0.5% ≤1.0% B3 |