Donfoam 812 HCFC-141B base lenhlanganisela polyols block Foam
Donfoam 812 HCFC-141B base lenhlanganisela polyols block Foam
ISINGENISO
Donfoam 812 lenhlanganisela polyether polyols esetshenziselwa umkhiqizo lePhure block Foam. I Foam kweseli iyunifomu, ongaphakeme conductivity ezishisayo, ezishisayo ukwahlukanisa ukusebenza kuhle, ilangabi cishe yizona ezisetshenziswa kabanzi ukusebenza kuhle, izinga lokushisa ongaphakeme kungekho zincipha ufa njll
Kabanzi inqubo zonke izinhlobo zomsebenzi ukwahlukanisa ezifana: ukwakha udonga lwangaphandle, indawo ebanda kakhulu, amathangi, amapayipi amakhulu njll
IMPAHLA NGOKWENYAMA
ukubukeka
viscosity Dynamic (25 ℃) mPa.S Ubuningi (20 ℃) g / ml lokushisa Isitoreji ℃ ngenyanga Isitoreji ukuzinza |
ophuzi Ukukhanya brown ketshezi esobala 250 ± 50 1.17 ± 0.1 10-25 6 |
ISILINGANISO ANCONYWA
izinto |
PBW |
Blend Polyether Polyol
Isocyanate |
100 130 |
TECHNOLOGY KANYE reactivity (ukubaluleka ngqo luyehluka kuye ukucutshungulwa izimo)
ukuxuba Manual |
|
Raw Material lokushisa ℃
Isikhunta lokushisa ℃ CT s GT s TFT s Mahhala Wugqinsi kg / m 3 |
20-25 Temperature Ambient (15-45 ℃) 35-60 140-180 240-260 26-28 |
foam ukusebenza
Into |
Test Standard |
Ukucaciswa |
Sekukonke Molding Wugqinsi
Udini Core Wugqinsi |
GB 6343 |
40-45kg / m 3 38-42kg / m |
Kuvaliwe-cell Ukukala |
GB 10799 |
≥90% |
Kokuqala conductivity ezishisayo (15 ℃) |
GB 3399 |
≤24mW / (MK) |
Amandla compressive |
GB / T8813 |
≥150kPa |
D Ukuzinza
24h -20 ℃ RH90 70 ℃ |
GB / T8811 |
≤1% ≤1.5% |
Amanzi Absorption Rate |
GB 8810 |
≤3% |
Flammability |
ASTM E84 |
class A |