MS resin 910R
MS resin 910R
ISINGENISO
910R kuyinto silane Ushintshe polyurethane resin esekelwe eliphezulu yamangqamuzana isisindo polyether, ekupheleni eneziqongo nge siloxane futhi equkethe amaqembu carbamate, sinezici umsebenzi omkhulu, akukho isocyanate dissociative, akukho kuphela, adhesion esihle nokunye.
910R sokwelapha mshini sokwelapha umswakama. Catalysts bayadingeka ekwakhiweni sealant. Ordinary organotin yelikhono (ezifana dibutyltin dilaurate) noma tin chelated (ezifana diacetylacetone dibutyltin) ingafinyelela izakhiwo ezinhle lokukhanda. Inani Kunconywa catalysts tin kuyinto 0.2-0.6%.
910R resin combinated nge plasticizer, nano-calcium carbonate, silane elihlangana ejenti kanye nezinye fillers kanye izithasiselo esingazilungisa imikhiqizo sealant esesikhundleni namandla eqine ka 1.0-4.0 MPA, 100% wemfihlo phakathi 0.3-2.0 MPA nokululama nokunwebeka ezingaphezu kuka-70%. 910R lungasetshenziswa ukulungiselela sealants esobala iziphi kabanzi isetshenziswa ekwakheni udonga Ingaphandle, ikhaya umhlobiso, zezimboni sealant nokunwebeka, ingcina nokunwebeka nokunye.
EZOBUCHWEPHESHE INDEX kwangu
Into |
Ukucaciswa |
indlela Test |
Appearrance |
Kungenambala ukuphaphatheka esobala ophuzi ketshezi viscous |
ezibukwayo |
Inani lombala |
50 Max |
APHA |
Viscosity (MPA · s) |
50 000-70 000 |
Brookfield viscometer ngaphansi 25 ℃ |
pH |
6.0-8.0 |
Isopropanol / isixazululo aqueous |
Umswakama okuqukethwe (% wt) |
0.1 Max |
Karl Fischer |
Ubuningi |
0.96-1.04 |
25 ℃ amanzi konga 1 |
PACKAGE ULWAZI
iphakethe Encane |
20 kg yensimbi sigubhu |
iphakethe okulingene |
200 kg yensimbi sigubhu |
iphakethe elikhulu |
1000kg PVC ton sigubhu |
UKUGCINWA
Indawo endaweni epholile futhi umoya place.Unopened ukulondolozwa ekamelweni temperature.The isikhathi isitoreji mkhiqizo 12 izimpahla months.Non-oluvuthayo, ngokuvumelana ezivamile ezokuthutha zamakhemikhali.