Wholesale Boxing Gloves System - Quasi MDI-terminated system – INOV
Wholesale Boxing Gloves System - Quasi MDI-terminated system – INOV Detail:
Quasi MDI-terminated PTMG system
DESCRIPTION
Component: DY2513 is consist by Components ABC. Component A is polyol, B is polyurethane prepolymer which ended up with isocynate, C is chain extender.
Characteristic: The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: This material was used to produce Polyurethane sieves, PU rollers, cleaning pigs (discs) and other elastomer.
SPECIFICATION
Type |
DY2513-B |
DY2513-A |
DY2513-C |
|||||
NCO/% |
13.1 |
|
|
|||||
Operation temperature /℃ |
45 |
50 |
45 |
|||||
Viscosity mPa·s/ |
800 |
1200 |
30 |
|||||
Prepolymer |
DY2513-B |
|||||||
Chain extender |
DY2513-A﹢DY2513-C |
|||||||
Hardness /shore A |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
95 |
DY2513-B(ratio, by weight ) |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
DY2513-A(ratio, by weight ) |
180 |
150 |
120 |
100 |
80 |
60 |
40 |
20 |
DY2513-C(ratio, by wight) |
5.7 |
7 |
8.4 |
9.3 |
10.2 |
11.1 |
12 |
12.9 |
Catalyst/total amount A+B+C % |
0.6 |
0.6 |
0.6 |
0.45 |
0.3 |
0.3 |
0.24 |
0.24 |
Mold temperature/℃ |
100 |
|||||||
Gel time/min |
2,30 |
2,30 |
2,20 |
2,20 |
2,30 |
2,30 |
2,10 |
2,10 |
Open Mold Time/ min |
60 |
50 |
40 |
40 |
40 |
40 |
40 |
40 |
Quasi MDI-terminated Polyester system
DESCRIPTION
It is used to produce Polyurethane sieves, PU rollers and other elastomer. It should be processed by mid-temperature casting machine.
The final product enjoys good anti resistance ability, good rebound. And the hardness can be adjusted by the different ratio. The color can be adjusted by pigment.
Application: automotive kits, pipe cleaners, etc., polyurethane large or small product components.
SPECIFICATION
Type |
DY3516-B |
DY3516-A |
DY3516-C |
|||||||
NCO/% |
16.5±0.2 |
|
|
|||||||
Operation temperature /℃ |
45 |
70 |
45 |
|||||||
Viscosity mPa·s/ |
700 |
730 |
30 |
|||||||
Prepolymer |
DY3516-B |
|||||||||
Chain extender |
DY3516-A+DY3516-C |
|||||||||
Hardness /shore A |
55 |
60 |
65 |
70 |
75 |
80 |
85 |
90 |
||
DY3516-B(ratio, by weight) |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
100 |
||
DY3516-A(ratio, by weight) |
380 |
180 |
160 |
130 |
110 |
100 |
80 |
60 |
||
DY3516-C(ratio, by weight) |
0 |
9.1 |
10 |
11.4 |
12.3 |
12.7 |
13.6 |
14.5 |
||
Catalyst/total amount A+B+C % |
0.4 |
0.4 |
0.4 |
0.4 |
0.3 |
0.3 |
0.3 |
0.3 |
||
Mold temperature/℃ |
100 |
|||||||||
Gel time/min |
5 |
5 |
5 |
5 |
5 |
4 |
4 |
4 |
||
Open Mold Time/ min |
50 |
35 |
35 |
30 |
30 |
30 |
30 |
30 |
||
Post cure time(90℃)/h |
16 |
AUTOMATIC CONTROL
The production is controlled by DCS system, and packing by automatic filling machine. Package is 200KG/DRUM Or 20KG/DRUM.
Product detail pictures:
Related Product Guide:
With this motto in mind, we've got become among essentially the most technologically innovative, cost-efficient, and price-competitive manufacturers for Wholesale Boxing Gloves System - Quasi MDI-terminated system – INOV , The product will supply to all over the world, such as: Amsterdam, Seattle, Bangalore, You can let us know your idea to develop unique design for your own model to prevent too much similar parts in the market! We will offer our best service to satisfy all your needs! Please contact us right away!
By Edwina from Sri Lanka - 2018.09.29 17:23
In our cooperated wholesalers, this company has the best quality and reasonable price, they are our first choice.
By Delia Pesina from Belgium - 2018.06.21 17:11