Seri PES/TDI

Pri FOB:0.5 dola ameriken - 9,999 dola ameriken / pyès

Kantite Minimòm pou Lòd:100 Moso/Moso

Kapasite Pwovizyon:10000 Moso/Moso pa Mwa

peyi orijin:Lachin

mak komèsyal:INOV

dite: rivaj A 60A - rivaj D 70D

Pwodwi a gen karakteristik bon operasyon, laj ranje dite, bon rezistans mete, rezistans ak ekselan pwopriyete mekanik.

Itilize pou fè divès pwodwi elastomè an poliyiretàn tankou wou kawoutchou, plak tamiz, gratwa, bag sele ak kawotchou.

Modèl	D3125	D3136	D3143	D3145	D3160	D3170
NCO/%	2.5±0.2	3.6±0.2	4.3±0.2	4.5±0.2	6.0±0.2	7.0±0.2
Eta a 20 ℃	solid blan
MOCA100g Prepolimè /g	7.2	10.5	12.5	13.2	17.2	20.0
Viskozite (85℃)/mPa·s	2800	1800	1300	1200	900	800
Tanperati melanj / ℃ (Prepolymer / MOCA)	85/120	85/120	80/120	80/120	75/120	75/120
Tan jèl /min	16	9	8	7.5	5	4.5
Tan apre vulkanizasyon (100 ℃) /h	10	10	10	10	10	10
Dite (Shore A)	76±2	85±2	92±2	91±2	96±2	97±2
100% Modil/MPa	3.4	4.2	6.3	6.7	11.5	18.0
300% Modil /MPa	4.1	8.3	11.8	12.5	21.3	35.7
Fòs tansyon / MPa	40	48	50	52	55	55
Elongasyon / %	700	670	630	610	530	410
Fòs chire / (KN/m)	55	75	105	95	124	152
Rebondisman / %	42	39	37	32	33	33
Dansite (24 ℃) / (g/ cm3)	1.25	1.26	1.27	1.27	1.29	1.29
Din mete /mm³	33	40	48	53	57	56

Modèl	D3230	D3236	D3243	D3245	D3249	D3260
NCO/%	3.0±0.2	3.6±0.2	4.3±0.2	4.5±0.2	4.9±0.2	6.0±0.2
Eta a 20 ℃	solid blan
MOCA 100g Prepolimè /g	8.6	10.5	12.5	13	14.5	17.5
Viskozite (85℃)/mPa·s	2500	2000	1400	1300	900	1200
Tanperati melanj / ℃ (Prepolymer / MOCA)	85/120	80/120	80/120	80/120	75/120	75/110
Tan jèl /min	5	4	4	3	3	2
Tan apre vulkanizasyon (100 ℃) /h	10	10	10	10	10	10
Dite (Shore A)	80±2	86	92±1	92±1	94±1	96 (52D)
100% Modil/MPa	4.0	5.1	6.1	6.8	7.3	12.2
300% Modil /MPa	6.5	9.8	11.4	12.6	13.4	20.9
Fòs tansyon / MPa	45	49	48	49	50	58
Elongasyon / %	750	690	650	600	580	530
Fòs chire / (KN/m)	61	88	99	100	106	132
Rebondisman / %	38	44	37	38	41	41
Dansite (24 ℃) / (g/ cm3)	1.25	1.26	1.27	1.27	1.27	1.28
Din mete /mm³	41	44	44	50	54	55