Series PES/TDI
duritia：litus A 60A – litus D 70D
Productum habet proprietates bonae operabilitatis, latae duritiae amplitudinis, bonae resistentiae attritionis, firmitatis, et excellentium proprietatum mechanicarum.
Adhibetur ad fabricanda varia producta elastomerica polyurethane, ut rotas gummeas, laminas cribrosas, radentes, anulos obturantes et pneumatica.
| Modellum | D3125 | D3136 | D3143 | D3145 | D3160 | D3170 |
| Subordinatus/% | 2.5±0.2 | 3.6±0.2 | 4.3±0.2 | 4.5±0.2 | 6.0±0.2 | 7.0±0.2 |
| Status ad 20 ℃ | solidum album | |||||
| MOCA100g Praepolymeri /g | 7.2 | 10.5 | 12.5 | 13.2 | 17.2 | 20.0 |
| Viscositas (85℃)/mPa·s | 2800 | MDCCC | 1300 | 1200 | 900 | DCCC |
| Temperatura mixtionis /℃ (Praepolymerum /MOCA) | 85/120 | 85/120 | 80/120 | 80/120 | 75/120 | 75/120 |
| Tempus gelificationis /min | 16 | 9 | 8 | 7.5 | 5 | 4.5 |
| Tempus post vulcanizationem (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 |
| Duritia (litus A) | 76±2 | 85±2 | 92±2 | 91±2 | 96±2 | 97±2 |
| Modulus/MPa 100% | 3.4 | 4.2 | 6.3 | 6.7 | 11.5 | 18.0 |
| Modulus 300% /MPa | 4.1 | 8.3 | 11.8 | 12.5 | 21.3 | 35.7 |
| Robur tensile /MPa | 40 | 48 | 50 | 52 | 55 | 55 |
| Elongatio / % | DCC | DCCLXX | DCXXX | DCX | 530 | 410 |
| Robur lacerationis / (KN/m) | 55 | 75 | 105 | 95 | 124 | CLII |
| Resilitio / % | 42 | 39 | 37 | 32 | 33 | 33 |
| Densitas (24℃) / (g/ cm3) | 1.25 | 1.26 | 1.27 | 1.27 | 1.29 | 1.29 |
| Detritio Din /mm³ | 33 | 40 | 48 | 53 | 57 | 56 |
|
|
|
|
|
|
|
|
| Modellum | D3230 | D3236 | D3243 | D3245 | D3249 | D3260 |
| Subordinatus/% | 3.0±0.2 | 3.6±0.2 | 4.3±0.2 | 4.5±0.2 | 4.9±0.2 | 6.0±0.2 |
| Status ad 20 ℃ | solidum album | |||||
| MOCA 100g Praepolymeri /g | 8.6 | 10.5 | 12.5 | 13 | 14.5 | 17.5 |
| Viscositas (85℃)/mPa·s | 2500 | MM | 1400 | 1300 | 900 | 1200 |
| Temperatura mixtionis /℃ (Praepolymerum /MOCA) | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/110 |
| Tempus gelificationis /min | 5 | 4 | 4 | 3 | 3 | 2 |
| Tempus post vulcanizationem (100℃) /h | 10 | 10 | 10 | 10 | 10 | 10 |
| Duritia (litus A) | 80±2 | 86 | 92±1 | 92±1 | 94±1 | 96 (52D) |
| Modulus/MPa 100% | 4.0 | 5.1 | 6.1 | 6.8 | 7.3 | 12.2 |
| Modulus 300% /MPa | 6.5 | 9.8 | 11.4 | 12.6 | 13.4 | 20.9 |
| Robur tensile /MPa | 45 | 49 | 48 | 49 | 50 | 58 |
| Elongatio / % | DCCCL | DCXC | DCCL | DC | 580 | 530 |
| Robur lacerationis / (KN/m) | 61 | 88 | 99 | centum | 106 | 132 |
| Resilitio / % | 38 | 44 | 37 | 38 | 41 | 41 |
| Densitas (24℃) / (g/ cm3) | 1.25 | 1.26 | 1.27 | 1.27 | 1.27 | 1.28 |
| Detritio Din /mm³ | 41 | 44 | 44 | 50 | 54 | 55 |