Donspray 504 HFC-245fa isi ngwakọta polyols
Donspray 504 HFC-245fa isi ngwakọta polyols
OKWU
DonSpray504 bụ ịgba ngwakọta polyols, ịfụ gị n'ụlọnga bụ 245fa kama HCFC-141B, ọ mkpatụ na isocyanate ka mepụtara ụfụfụ nke nwere magburu onwe arụmọrụ, nke ndị dị ka ndị,
1) ezi na Ime Otu mkpụrụ ndụ
2) ala thermal conductivity
3) zuru okè ire ọkụ na-eguzogide
4) ọma ala-okpomọkụ akụkụ kwụsie ike.
Ọ na-emetụta ihe nile di iche iche nke kwes mkpuchi engineering nke na-eji ịgba technology, dị ka oyi na-atụ ụlọ, ite, nnukwu-ọnụ ọgụgụ pipelines na-ewu ụlọ metope wdg
nkịtị onwunwe
ọdịdị |
Icha mmirimmiri edo edo ka aja aja viscous mmiri mmiri |
Hydroxyl Uru mgKOH / g |
200-300 |
Dynamic viscosity (25 ℃) mPa.S |
100-200 |
Specific ndọda (20 ℃) g / ml |
1.12-1.20 |
Nchekwa okpomọkụ ℃ |
10-25 |
Nchekwa kwụsie ike ọnwa |
6 |
na-atụ aro ruru
Ngwaọrụ |
pbw |
DonSpray 504 ngwakọta polyols |
100 g |
Isocyanate MDI |
100-105g |
Reactivity Njirimara (The okpomọkụ nke usoro bụ 20 ℃, na kpọmkwem uru iche iche dabere na nhazi ọnọdụ)
Ude Time s |
3-5 |
Jel Time s |
6-10 |
ụfụfụ arụmọrụ
ihe |
metric Unit |
Imperial Unit |
||
ịgba njupụta | GB 6343 | ≥35kg / m 3 | ASTM D 1622 | ≥2.18 lb / ft3 |
Mechiri emechi-cell Rate | GB 10799 | ≥90% | ASTM D 1940 | ≥90% |
Mbụ Kwes conductivity (15 ℃) | GB 3399 | ≤24mW / (Mak) | ASTM C 518 | ≥2.16 / inch |
compressive Ike | GB / T8813 | ≥150kPa | ASTM D 1621 | ≥21.76PSI |
nyagide Ike | GB / T16777 | ≥120kPa | ASTM D 1623 | ≥17.40PSI |
Dimentional Kwụsie 24h -20 ℃ | GB / T8811 | ≤1% | ASTM D 2126 | ≤1% |
24h 70 ℃ | ≤1.5% | ≤1.5% | ||
Water Absorption | GB 8810 | ≤3% | ASTM E 96 | ≤3% |
Fire-emegide | GB 8624 | Class B2 | ASTM D2863-13 | Class B2 |
ngwugwu
220kg / drum ma ọ bụ 1000kg / IBC, 20,000kg / flexi tank ma ọ bụ ISO tank.