High Performance Polymer Inov PPG Rigid Polyol Polyether
Kosemi ma jara
Ọrọ Iṣaaju
Awọn jara ti polyether polyols wa ni pese sile pẹlu o yatọ si functionalities, hydroxyl iye ati viscosities da lori yatọ si initiators. O kun lo ninu awọn gbóògì ti polyurethane kosemi foomu eto. Yatọ si awọn akojọpọ le wa ni ṣe gẹgẹ bi o yatọ si aini ti awọn onibara fun eto ohun elo lati gba o yatọ si išẹ.
APPLICATION
Awọn polyurethane kosemi foomu eto pese sile nipa lilo yi jara ti polyether polyol wa ni o kun lo fun producing firiji firisa, opo idabobo ohun elo ti, polyurethane ipanu nronu, sokiri idabobo ohun elo, igi imitation ohun elo ti, oorun ti ngbona ohun elo ti, ni erupe ile ohun elo ati awọn ati be be lo
Jijẹmọ data dì
Sucrose-bẹrẹtàbí polyether polyols fun kosemi a ma mu
brand |
awọ (GD) |
OHV (MgKOH / g) |
iki (MPa.s / 25 ℃) |
H 2Eyin akoonu (%) |
acid Iye (MgKOH / g) |
PH |
K + (Mg / Kg) |
ohun elo |
|||||||
firiji |
Pipe idabobo |
ipanu nronu |
sokiri foomu |
Wood imitation |
oorun ti ngbona |
Ologbele-kosemi foomu |
Omi-fifun |
||||||||
INOVOL R8345 |
≤9 |
440-460 |
6000-10000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★★ |
★ |
★★★ |
★ |
★ |
★ |
|
|
INOVOL R8336 |
≤9 |
350-370 |
2500-4000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★ |
★ |
★ |
|
★★ |
|
|
★★★ |
INOVOL R8315 |
≤10 |
430-470 |
15000-2000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★★ |
|
★★ |
|
|
|
|
|
INOVOL R8348 |
≤10 |
470-510 |
6000-10000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★ |
★ |
★★ |
★ |
|
|
|
|
INOVOL R8238 |
≤9 |
365-395 |
10000-12500 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★★★ |
★ |
★★ |
|
|
|
|
|
INOVOL R8243 |
≤9 |
400-460 |
2500-4000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★★ |
★★ |
★ |
|
★ |
|
|
★ |
INOVOL R8037 |
≤10 |
360-390 |
20000-35000 |
≤0.2 |
≤0.3 |
5-8 |
≤20 |
★★ |
|
★ |
|
★ |
|
|
|
Sorbitol-initiatied polyether polyols fun kosemi a ma mu
brand |
awọ (GD) |
OHV (MgKOH / g) |
iki (MPa.s / 25 ℃) |
H 2Eyin akoonu (%) |
acid Iye (MgKOH / g) |
PH |
K + (Mg / Kg) |
ohun elo |
|||||||
firiji |
Pipe idabobo |
ipanu nronu |
sokiri foomu |
Wood imitation |
oorun alapapo |
Ologbele-kosemi foomu |
Omi-fifun |
||||||||
INOVOL R6205 |
≤8 |
355-395 |
2000-3000 |
≤0.2 |
≤0.5 |
5-8 |
≤20 |
★★★ |
★ |
★ |
|
★★ |
★ |
|
★ |
INOVOL R6207 |
≤8 |
440-480 |
12500-16500 |
≤0.2 |
≤0.5 |
5-8 |
≤20 |
★★★ |
★★ |
★★★ |
|
★★ |
★★ |
|
|
INOVOL R6350 |
≤8 |
480-520 |
4500-6500 |
≤0.2 |
≤0.5 |
5-8 |
≤20 |
|
★ |
★★ |
★ |
|
|
|
|
INOVOL R6048 |
≤8 |
455-505 |
35000-45000 |
≤0.2 |
≤0.5 |
5-8 |
≤20 |
★★ |
|
★★ |
|
|
|
|
|
Tabi-bẹrẹtàbí polyether polyols fun kosemi a ma mu
brand |
awọ (GD) |
OHV (MgKOH / g) |
iki (MPa.s / 25 ℃) |
H 2Eyin akoonu (%) |
acid Iye (MgKOH / g) |
PH |
K + (Mg / Kg) |
ohun elo |
|||||||
firiji |
Pipe idabobo |
ipanu nronu |
sokiri foomu |
Wood imitation |
oorun alapapo |
Ologbele-kosemi foomu |
Omi-fifun |
||||||||
INOVOL R403 |
≤100 (APHA) |
745-775 |
1400-2400 (50 ℃) |
≤0.15 |
- |
10-13 |
- |
« |
|
«« |
«« « |
|
|
|
|
INOVOL R405 |
≤8 |
435-465 |
4000-5500 |
≤0.15 |
- |
10-13 |
≤20 |
«« |
|
« |
|
|
|
«« |
|