Polyether/TDI-type prepolymeer
De produkten hawwe goede wearbestindigens, wetterbestindigens, skimmelbestindigens, poerbêste meganyske eigenskippen, en kleur kin tafoege wurde om de kleur oan te passen. It wurdt brûkt om polyurethaanprodukten te meitsjen lykas rubberen stokken, rubberen tsjillen, platen, rubberen coatings en ferskate ûnderdielen.
| Model | D1140 | D1145 | D1155 | D1160 | D1180 | D1185 |
| NCO/% | 4.0±0.2 | 4,5 ± 0,2 | 5,5 ± 0,2 | 6.0±0.2 | 8.0±0.2 | 8,5 ± 0,2 |
| Steat by 20 ℃ | Kleurleaze transparante floeistof | |||||
| MOCA100g Prepolymeer /g | 11.5 | 13.0 | 16.0 | 17.5 | 23 | 24.0 |
| Viskositeit (85℃)/mPa·s | 340 | 300 | 250 | 250 | 450 | 400 |
| Mingtemperatuer / ℃ (Prepolymeer/MOCA) | 80/120 | 80/120 | 80/120 | 80/120 | 75/110 | 75/110 |
| Geltiid /min | 10 | 9.5 | 9 | 6 | 2 | 2 |
| Nei-vulkanisaasjetiid (100 ℃) /oere | 10 | 10 | 10 | 10 | 10 | 10 |
| Hurdens (Shore A) | 78±2 | 82±2 | 88±1 | 92±1 |
|
|
| Hurdens (Shore D) |
|
|
|
| 70±1 | 78±1 |
| 100% Modulus/MPa | 4.6 | 5.0 | 5.5 | 6.2 | 23.2 | 32.5 |
| 300% Modulus / MPa | 8.2 | 9.2 | 13.0 | 20.8 | - | - |
| Treksterkte / MPa | 27 | 28 | 32 | 35 | 39 | 42 |
| Ferlinging / % | 550 | 480 | 400 | 350 | 230 | 180 |
| Skuorreftichheid / (KN/m²) | 46 | 55 | 76 | 78 | 123 | 145 |
| Rebound / % | 28 | 24 | 24 | 33 | 40 | 51 |
| Dichtheid (24 ℃) / (g/ cm3) | 1.11 | 1.12 | 1.14 | 1.14 | 1.18 | 1.18 |
| Din wear /mm³ | 148 | 112 | 109 | 141 | 131 | 89 |
| Model | D1230 | D1235 | D1240 | D1245 | D1250 | D1262 | D1265 | D1270 |
| NCO/% | 3.0±0.1 | 3,5 ± 0,1 | 4.0±0.1 | 4,5 ± 0,2 | 5.0±0.2 | 6,2±0,2 | 6,5 ± 0,2 | 7.0±0.2 |
| Steat by 20 ℃ | Kleurleaze transparante floeistof | |||||||
| MOCA 100g Prepolymeer /g | 8.6 | 10.3 | 11.5 | 13 | 14.5 | 18 | 19 | 20.5 |
| Viskositeit (85℃)/mPa·s | 200 | 250 | 350 | 400 | 450 | 240 | 300 | 400 |
| Mingtemperatuer / ℃ (Prepolymeer/MOCA) | 85/120 | 85/120 | 80/120 | 80/120 | 80/120 | 75/120 | 75/120 | 75/120 |
| Geltiid /min | 9 | 5 | 4.5 | 4 | 3.5 | 3 | 2.5 | 2 |
| Nei-vulkanisaasjetiid (100 ℃) /oere | 10 | 10 | 10 | 10 | 10 | 10 | 10 | 10 |
| Hurdens (Shore A) | 70±2 | 78±2 | 84±2 | 86±2 | 90±1 | 94±1 | 97±1(53D) | 60D±1 |
| 100% Modulus/MPa | 2.1 | 4.2 | 5.4 | 5.9 | 8.9 | 9.2 | 15.2 | 15.8 |
| 300% Modulus / MPa | 3.0 | 6.3 | 10.0 | 10.3 | 14.6 | 16.8 | 24.6 | 23 |
| Treksterkte / MPa | 7 | 10 | 19 | 21 | 31 | 32 | 35 | 33 |
| Ferlinging / % | 600 | 550 | 500 | 480 | 460 | 450 | 440 | 420 |
| Skuorreftichheid / (KN/m²) | 34 | 44 | 53 | 57 | 73 | 78 | 95 | 120 |
| Rebound / % | 50 | 48 | 41 | 31 | 30 | 31 | 41 | 43 |
| Dichtheid (24 ℃) / (g/ cm3) | 1.08 | 1.09 | 1.11 | 1.13 | 1.14 | 1.15 | 1.16 | 1.17 |
| Din wear /mm³ | 163 | 159 | 116 | 157 | 135 | 117 | 143 | 135.6 |