Polyester-based TPU-Hotmelt Film
Hardness: Shore A 70 – Shore A 97
Characteristics: Good adhesion to TPU, nylon, PVC, cloth, leather and other materials, and after bonding, it has the characteristics of high bonding strength, high toughness, wear resistance and good elasticity
Applications: Calendered film, Milled powder, Transparent film, fabric lamination, Shoe materials, Seam sealing tapes etc.
|
Items |
Hardness |
Tensile Strength |
Softening point |
Melt Flow Rate |
Laminating Temperature |
Tack Free Time |
|
Standard |
ASTM D2240 |
ASTM D412 |
ASTM D36 |
ASTM D1238 |
INOV Method |
INOV Method |
|
Unit |
Shore A |
MPa |
℃ |
g/10min |
℃ |
min |
|
T5160 |
97 |
18 |
75 |
33-36 |
70-80 |
3 |
|
T5260 |
97 |
20 |
80 |
16-18 |
75-85 |
3.5 |
|
T5260H |
97 |
23 |
85 |
11-13 |
80-90 |
4 |
|
T6195 |
97 |
25 |
130 |
20-25 |
110-140 |
10 |
|
T6185 |
97 |
28 |
140 |
15-20 |
120-150 |
12 |
|
Items |
Hardness |
Tensile Strength |
Elongation |
Flow Beginning Temperature |
Softening point |
Laminating Temperature |
|
Standard |
ASTM D2240 |
ASTM D412 |
ASTM D412 |
INOV Method |
ASTM D36 |
INOV Method |
|
Unit |
Shore A |
MPa |
% |
℃ |
℃ |
℃ |
|
B480 |
81 |
16 |
800 |
95 |
115 |
120-140 |
|
B485 |
85 |
18 |
950 |
103 |
125 |
130-150 |
|
T5170 |
72 |
18 |
850 |
105 |
126 |
130-150 |
|
T5170-1 |
72 |
18 |
850 |
105 |
126 |
100-150 |
|
T5175 |
77 |
19 |
800 |
113 |
133 |
140-160 |
|
T5175-1 |
77 |
19 |
800 |
113 |
133 |
110-160 |
|
T5185-10 |
82 |
24 |
850 |
122 |
146 |
140-160 |
|
T5185-9 |
82 |
24 |
850 |
122 |
146 |
120-170 |
|
T5190 |
91 |
19 |
750 |
115 |
133 |
140-160 |